Surgical implant Ti13Nb13Zr titanium bar. Nb, Zr elements are high Nb, and the addition of Zr alloy is advisable; the hardness value of the alloy in the β phase zone is slightly higher than that in the α + β phase zone. The hardness value of solution treatment; when the aging system is 510°C, 6h, and the processing deformation is greater than 50%, the overall performance of the material is the best.
| Item name | Ti13Nb13Zr titanium bar |
| Standard | ASTM F67/ASTM F136/ISO5832-2/ISO5832-3 |
| Grade | GR5 Ti6AL4V ELI,Gr236AL7Nb,13Nb13Zr |
| Dimension | OD*L (2-100)*(Max3000)mm |
| Features | Light weight, excellent corrosion resistivity, strongly heat-resistance, high strength. |
| Inspection | Ultrasonic testing, Hydrostatic testing, Flattening testing, visual surface inspection, Dimensional inspection, tensile properties inspection and Chemical elements analysis. |
Physical Properties:
|
Grade |
Status |
Tensile Strength |
Yield Strength |
Elongation |
Area of Reducation |
||
|
Ksi |
Mpa |
Ksi |
Mpa |
% |
|||
|
GR1 |
Annealed
|
35 |
20 |
25 |
170 |
24 |
30 |
|
GR2 |
50 |
345 |
40 |
275 |
20 |
30 |
|
|
GR3 |
65 |
450 |
55 |
380 |
18 |
30 |
|
|
GR4 |
80 |
550 |
70 |
483 |
15 |
25 |
|
|
TI-6AL-4VELI |
125 |
860 |
115 |
795 |
10 |
25 |
|
|
Ti6AL7Nb |
130.5 | 900 |
116.8 |
800 |
10 |
25 |
|
|
Ti13Nb13Zr |
ageing125 Solid 800 Not annealed 800
|
860
550
550 |
105 500 500 |
725 345 345 |
8 15 8 |
15 30 15 |
|
For more information on Ti13Nb13Zr titanium bar, please contact us.